PETG-CF Settings for Markforged Onyx Pro
Recommended slicer settings for printing PETG-CF on the Markforged Onyx Pro (320 x 132 x 154 mm build volume, 200 mm/s max speed, direct drive extruder).
غير متوافقintermediate
غير متوافق
The max bed temperature of 0°C is below the recommended 70°C for PETG-CF. Adhesion may be poor without additional bed adhesion aids.
| Filament Nozzle Requirement | 230-260°C |
| Printer Max Nozzle | 280°C |
| Filament Bed Requirement | 70-80°C |
| Printer Max Bed | N/A |
ما الذي يجب فعله بدلاً من ذلك
- Your printer's bed maxes out at 0°C, but PETG-CF needs at least 70°C for reliable adhesion.
- Try a compatible filament for your Markforged Onyx Pro — PLA, PETG, and ABS are good options.
- If you need PETG-CF specifically, you'll need a printer with a hotend capable of 230°C+ nozzle.
PETG-CF Requirements
PETG-CF Properties
| Nozzle Range | 230-260°C |
| Bed Range | 70-80°C |
| Speed Range | 30-50 mm/s |
| Difficulty | intermediate |
| Enclosure | Not needed |
| Drying | 65°C / 8h |
Markforged Onyx Pro Specs
| Build Volume | 320 x 132 x 154 mm |
| Max Speed | 200 mm/s |
| Max Nozzle Temp | 280°C |
| Max Bed Temp | N/A |
| Extruder | Direct Drive |
PETG-CF في لمحة
نقاط القوة
- Significantly stiffer than standard PETG
- Professional matte surface finish
- Reduced warping compared to plain PETG
- Good chemical and moisture resistance
- Excellent for functional brackets, jigs, and fixtures
نقاط الضعف
- Requires hardened steel nozzle (carbon fibers destroy brass)
- More brittle than standard PETG (reduced flexibility)
- Must use 0.5mm+ nozzle to prevent clogging
- Slower print speeds required than standard PETG
- Higher cost than plain PETG ($30-45/kg)
تريد إعدادات AI مخصصة؟
صِف إعدادك الدقيق وما تطبعه. يُنشئ خبير AI في 3DSearch إعدادات تقطيع مخصصة لطابعتك Markforged Onyx Pro مع PETG-CF خلال ثوانٍ.
جرّب 3DSearch →المصادر: Based on manufacturer specifications and community recommendations, community testing data, manufacturer recommended ranges. تم حساب القيم من مواصفات الفيلامنت وحدود عتاد الطابعة.